Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

Wuxi Zhanlu International Trade Co., Ltd
Trust Seal
Verified Supplier
Credit Check
Supplier Assessment
Contact Now
    Buy cheap Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod from wholesalers
     
    Buy cheap Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod from wholesalers
    • Buy cheap Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod from wholesalers

    Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

    Ask Lasest Price
    Brand Name : Zhanlu
    Model Number : D2
    Price : Consultation
    Payment Terms : L/C, T/T
    Supply Ability : Consulting service
    Delivery Time : 5-8Workdays
    • Product Details
    • Company Profile

    Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod

    D2 Die steel ASTM A681 - 2008 Hot rolled / bright round bar

    D2 steel has high wear resistance, micro-deformation cold working die steel, and wind-hardened tool steel, with carbon content up to 1.5%, chromium content up to 11.5%, and hardness up to 60HRC after heat treatment. D2 steel, such as silicon steel sheet punching die, cold cutting scissors, trimming die, etc. High wear resistance, vacuum heat treatment to HRC60 ° - 62 °, excellent processing performance.


    Supply Form & Size

    Form of SupplySize(mm)Length(mm)
    Round bar6.0mm-500mm2.5m-10m

    Chemical Composition&Related Specifications

    GradeCMnCrMoVCoPSSi
    D21.4-1.6≤0.611.0-13.00.70-1.20≤1.1≤1.0≤0.30≤0.30≤0.60

    Brand comparison table

    AISI/SAEDIN/ENBSJIS/KSChina
    D2X153CrMoV12X153CrMoV12SKD11Cr12Mo1V1

    Mechanical Property

    Heat treatment specification

    Quenching, 820 ± 15 ℃ preheating, 1000 ± 6 ℃ (salt bath) or 1010 ± 6 ℃ (furnace controlled atmosphere) heating, heat preservation for 10-20 min, air cooling, 200 ± 6 ℃ tempering
    Quenching:Slowly raise the temperature of the workpiece to 600 ℃, hold it for 20 min for the first preheating, and then rise to 850 ℃ after the average temperature, and hold it for 30 min for the second preheating, and finally raise the temperature to 1020~1040 ℃, hold it for 25~40 min, and then discharge it for air cooling.
    Stress relief annealinAfter rough machining, the workpiece shall be heated to 600~650 ℃, kept for 2h, cooled to 500 ℃ with the furnace, and then discharged for air cooling


    Product Tags:

    d2 steel bar

      

    d2 round bar

      

    d2 material round bar

      
    Quality Material D2 Tool Steel Round Bar 1-3/4 ASTM A681 2008 Die Steel Rod for sale
    Inquiry Cart 0
    Send your message to this supplier
     
    *From:
    *To: Wuxi Zhanlu International Trade Co., Ltd
    *Subject:
    *Message:
    Characters Remaining: (0/3000)